Tan, Ezgi; Snee, Preston T.; Danışman‑Kalındemirtaş, Ferdane

Anticancer theranostic nanocarriers have the potential to enhance the efficacy of pharmaceutical evaluation of drugs. Semiconductor nanocrystals, also known as quantum dots (QDs), are particularly promising components of drug carrier systems due to their small sizes and robust photoluminescence properties. Herein, bright CdZnSeS quantum dots were synthesized in a single step via the hot injection method. The particles have a quasi-core/shell structure as evident from the high quantum yield (85 %), which decreased to 41 % after water solubilization. These water solubilized QDs were encapsulated into gallic acid / alginate (GA-Alg) matrices to fabricate imaging QDs@mod-PAA/GA-Alg particles with enhanced stability in aqueous media. Cell viability assessments demonstrated that these nanocarriers exhibited viability ranging from 63 % to 83 % across all tested cell lines. Furthermore, the QDs@mod-PAA/GA-Alg particles were loaded with betulinic acid (BA) and ceranib-2 (C2) for in vitro drug release studies against HL-60 leukemia and PC-3 prostate cancer cells. The BA loaded QDs@mod-PAA/GA-Alg had a half-maximal inhibitory concentration (IC50) of 8.76 μg/mL against HL-60 leukemia cells, which is 3-fold lower than that of free BA (IC50 = 26.55 μg/mL). Similar enhancements were observed with nanocarriers loaded with C2 and simultaneously with both BA and C2. Additionally, BA:C2 loaded QDs@mod-PAA/GA-Alg nanocarriers displayed a similar enhancement (IC50 = 3.37 μg/mL compared against IC50 = 11.68 μg/mL for free BA:C2). The C2 loaded QDs@mod-PAA/GA-Alg nanocarriers had an IC50 = 2.24 μg/mL against HL-60 cells. C2 and BA loaded QDs@mod-PAA/GA-Alg NCr had IC50 values of 7.37 μg/mL and 24.55 μg/mL against PC-3 cells, respectively.

Gürses, A.; Karaca, S.; Doǧar, Ç.; Bayrak, R.; Açikyildiz, M.; Yalçin, M.

In this study, adsorption of methylene blue onto clay was investigated. The effect of adsorption time and temperature on the adsorption process was studied. To reveal the adsorptive characteristics of the clay studied, porosity and BET surface area measurements were made. It was observed that the adsorption capacity decreases with increasing temperature, and adsorption equilibrium was attained within 1 h. It was found that the data fit well to Langmuir, Halsey, Henderson, and Harkins-Jura models but experimental data deviate significantly from BET and Freundlich models at especially high concentrations. Furthermore, isosteric adsorption enthalpy and entropy are calculated as -7.99 kJmol-1 and 25.41 JK-1mol -1, respectively.