Akar, Türker; Ä°çen, Gülşah

Objective: This study aimed to investigate the effects of laser irradiation applied to zirconia and tooth surfaces on shear bond strength (SBS) compared with acid etching and sandblasting. Background: The effect of laser irradiation on the bond strength between zirconia and adhesives is a controversial issue for dentin surface treatments. In addition, the effects of different combinations of surface treatments to increase adhesion on both the zirconia and dentin surfaces remain unclear. Materials and methods: A total of 90 tooth samples were assigned into groups according to various pretreatments: control group was left untreated, acid etching, and Erbium, Chromium:Yttrium Scandium Gallium Garnet (Er,Cr:YSGG) laser irradiation group (15 Hz, 2 W). In addition, the zirconia specimens were separated into three groups (n = 10) according to the different surface treatments performed: sandblasting (120 μm Al2O3), Er,Cr:YSGG laser (15 Hz, 2 W), and as untreated surface. The zirconia samples were cemented to the dentin surface using dual-cure resin cement and subjected to an SBS test at a speed of 0.5 mm/min under a universal testing machine until fractures occurred in the bonding surface. Results: The highest SBS values were observed in Group tooth acid (TA)-zirconia Er,Cr:YSGG laser (ZL), followed by Group tooth Er,Cr:YSGG laser (TL)-zirconia sandblasting (ZS) and Group TA-zirconia control (ZC). The lowest SBS values were found in Group TA-ZS. Significant intergroup difference was noted between Group TA-ZL, Group tooth control (TC)-ZC, Group TL-ZS, and Group TC-ZC. However, no significant difference was noted between Group TA-ZL, Group TL-ZS, and Group TA-ZC. Conclusions: Acid etching and laser treatments applied to the dentin and zirconia surfaces were found to be effective techniques for improving the zirconia-dentin bond, respectively. Clinical Trial Registration number: 33216249-604.01.02-E.24308.

Ustun, Ozlem; Akar, Turker; Kirmali, Omer

Objective: The purpose of this study was to evaluate the effects of Er,Cr:YSGG laser irradiation with different energy powers versus sandblasting for enhancing the tensile bond strength (TBS) between titanium implant abutments (IAs) and resin cements. Background data: Clinical decementation of prosthetic restorations often occurs, particularly on short IAs. Increasing the bonding area on the IA surface can enhance the function and longevity of the superstructure. Materials and methods: Fifty dental IAs were used in solid form and randomly assigned to five groups (n = 10 each) for the following different pretreatments: control group was left untreated, a laser operating at 2.78 μm wavelength with different energy powers (1, 2, and 3 W) was used for three laser groups, and 50 μm alumina particles were applied to the abutment surface for the sandblasting group. Fifty metal substructures that had an occlusal metal O-ring were cast and cemented to all abutments using dual-cure resin cement. Test specimens were then subjected to thermal cycling. TBS tests were performed with a universal testing machine. The specimens' surface topography and roughness were evaluated with scanning electron microscope, and energy dispersive spectroscopy (EDS) was used to measure the elemental profiles of each specimen. Data were analyzed using a one-way analysis of variance/Kruskal-Wallis test at a significance level of p < 0.05. Results: Surface treatments affected the surface roughness and TBS of the IA. The sandblasting group showed the highest bond strength values (510.77 ± 60.86 N) and followed by the 2 W group (279.07 ± 37.9 N). In EDS analysis, no elemental components other than titanium and oxygen were observed, except for in the sandblasting group. Conclusions: Sandblasting and 2 W laser treatment increased the surface roughness of the IA, which could contribute to the increased interfacial bond strength between the IA and resin cement.