Akpinar, Iclal Avinc; Gültekin, Kürşat; Akpinar, Salih; Gürses, Ahmet; Ozel, Adnan

In this study, the mechanical properties of single lap joints prepared by adding nanoclays with different properties into adhesives with different characteristics (toughened, flexible, paste-type, and rigid) were experimentally investigated. Single lap joints and bulk specimens were produced using DP460, DP125, Araldite 2015, and AV138 as adhesives. High-concentration hydrocarbon-doped organo-clay (HDOC-1) obtained from Çankırı, low-concentration hydrocarbon-doped organo-clay (HDOC-2) obtained from Erzurum, and organo-clay (OC) were incorporated into the adhesives as reinforcements at two different concentrations (1% and 2% wt.). The aluminum alloy AA2024-T3 was used as the adherend material. Evaluation of experiment results showed that both the characteristics of the adhesive (toughened, flexible, paste-type, and rigid) and the different forms of clays significantly influenced failure loads of the joints. Moreover, increasing or decreasing the amount of clay added into the adhesive also affected failure loads of the joints; 1% wt. reinforcement provided the best results.

Akpinar, Iclal Avinc; Gürses, Ahmet; Akpinar, Salih; Gültekin, Kürşat; Akbulut, Hamit; Ozel, Adnan

In recent years, findings in nanoscience and nanotechnology have deeply influenced many disciplines including the material and mechanical sciences. Polymers including nanostructures have attracted attention as their adoptions in general engineering composites have yielded efficient results. In this study, three different two-component (epoxy-hardener) adhesives were doped with graphene nanoplatelets, graphene oxide nanoplatelets, carbon nanotube, and fullerene C60 at three different rates (0.5%, 1%, and 2% by weight) and the mechanical and thermal properties of the nanocomposite adhesives were examined. The nanocomposite adhesives’ mechanical properties were analyzed via tensile tests and thermal properties were analyzed via Differential Scanning Calorimeter (DSC) thermograms and Fourier Transform Infrared Spectroscopy (FT-IR) spectra. Results showed that doping nanostructures improve the stress-strain capacity of the adhesives. Both mechanical and thermal properties of the nanocomposite adhesives seem to change depending on the amount of nanostructure. Additionally, DSC and FT-IR curves showed an agreement with these improvements in the adhesives’ mechanical properties.

Gültekin, KürŞat; Akpinar, Salih; Özel, Adnan; Öner, GülŞah Alar

This article presents the experimental and numerical results of adhesively bonded hybrid single-lap joint (SLJ) geometry with different configurations of lower and upper adherends subject to a four-point bending test. AA2024-T3 aluminium alloy and carbon/epoxy composites with different lamina numbers and four different stacking angles as adherend and two-part liquid, structural adhesive DP 125 as paste adhesive were used. In the experimental studies, three different types of SLJs were produced using lower material that had a constant thickness of AA2024-T3 aluminium alloy and upper material of composite material that had different numbers of layers and four different stacking sequences ([0], [0/90], [45/−45], [0/45/−45/90]). In the numerical analysis, stress analyses of the SLJs were performed with a three-dimensional non-linear finite element method and the composite adherends were assumed to behave as linearly elastic materials, while the adhesive and aluminium adherend were assumed to be non-linear. Consequently, the change of stacking sequence and thickness of the composite in adhesively bonded SLJs altered the location of the neutral axis in the joint. This situation substantially influences the load-carrying capacity of the joint.